Protective coatings for polyimide composites

ABSTRACT

The service life of fiber-reinforced polyimide composites in a high temperature oxidative environment is extended by coating with a polyimide coating precursor solution that is synthesized by reacting an aromatic dianhydride with an aromatic diamine in a non-reactive solvent. The reactive solution is heated to a temperature sufficent to reduce its viscosity prior to its use as a coating. Preferably, a mixture of meta-phenylenediamine and para-phenylenediamine is reacted with biphenyldianhydride in n-methyl pyrrolidinone solvent and thereafter heated to between about 50° C. (122° F.) and 150° C. (302° F.) under nitrogen while stirring for a time sufficient to obtain a polyamic acid polyimide precursor coating solution having a Brookfield viscosity of from about 500 to about 5000 cP and a solids content of from about 5 to about 35 weight percent.

This invention relates to protective coatings for polyimide composites and methods of synthesis of such coatings.

BACKGROUND OF THE INVENTION

Over the past twenty-five years, advanced polymeric matrix composites have become established as high-performance structural materials, but composite oxidation limits service lifetimes at elevated temperature. Protective coatings that provide improved thermo-mechanical performance at high temperatures are needed to effectively utilize polymeric matrix composites in future aerospace applications. Protection of machined surfaces, especially machined edges having exposed fibers, from rapid oxidation, is especially needed.

One widely used polymeric matrix material is an addition-type polyimide known as PMR-15. Due to PMR-15's relatively high service temperature, processing ease and good thermal stability, it has become the polyimide "standard" for the aerospace industry. However, due to oxidation, a carbon fiber/PMR-15 composite will lose about five to seven percent in compression strength for every one percent in weight loss.

A coating of a fluorinated polyimide known as L30N has been shown to protect carbon fiber/PMR-15 composites from erosion at elevated temperature. The L30N resin is currently commercially available from TRW, Inc. of Redondo Beach, Calif. as PFPI.

Thin ceramic coatings have also been investigated as oxygen barriers to protect PMR-15 substrates at elevated temperatures. In most cases, these coatings did protect the composite surface from oxidative degradation over several hundred hours of constant thermal conditioning up to 380° C. (716° F.). However, such ceramic coatings have an extreme mismatch in the coefficient of thermal expansion (CTE) between the ceramic protective film and the polymeric composite. The internal or compressive stresses that are formed in the ceramic coating during cooling in the CVD reactor are significant enough to cause the protective layer to crack or delaminate from the composite substrate. This CTE problem is very significant when a composite component undergoes thermal cycling during service, commonly resulting in spalling of the coating. In order to reduce the thermal stresses at the composite/coating interface, compliant layers consisting of different fluorinated high-temperature polyimides have been used.

According to the invention, there is provided a polyamic acid polyimide precursor solution suitable for use as a coating to protect polyimide substrates against thermally induced oxidative degradation. Coatings according to the invention may be sprayed or brushed on to the substrate. Following application of the polyamic acid solution, the coated substrate is heated to convert the coating to a polyimide.

The coating solution may be prepared by by reacting an aromatic dianhydride with an aromatic diamine in a non-reactive solvent and heating the solution to a temperature between 50° C. and 150° C., more preferably from 80° C. to 145° C. In certain emodiments, the reactive coating solution is preferably heated until a viscosity drop occurs. The heating may be carried out at at elevated temperature above 50° C. in an inert atmosphere for a time sufficient to obtain a polyamic acid having a Brookfield viscosity of from about 500 to about 5000 cP, more preferably about 600 to about 2000 cP and a solids content of from about 5 to about 35 weight percent, more preferably from about 10 to about 30 weight percent. Suitable material has been obtained by heating the reactive mixture under nitrogen near but not at reflux for about one hour in in n-methyl pyrrolidinone solvent (NMP)

Although meta-phenylenediamine or para-phenylenediamine can be used individually, a mixture of meta-phenylenediamine and para-phenylenediamine preferably is used in combination with 3,3'4,4'-biphenyldianhydride. The meta-phenylenediamine isomer is believed to provide a "kink" in the polymer chain backbone as contrasted with a straight polymer chain backbone which is expected if only para-phenylenediamine is used. This was done in an attempt to create a less brittle and more ductile coating than would result if only para-phenylenediamine was used. The ratio of meta-PDA to para-PDA is preferably from about 90:10 to about 15:85, and more preferably, from about 75:25 to about 50:50.

It is believed that 2,3,3',4'-biphenyldianhydride can be used as a total or partial substitute for 3,3'4,4'-biphenyldianhydride.

It is believed that a suitable coating can be made by reacting 3,3',4,4'-biphenyldianhydride (BPDA) with a 0.8 to 1.2:1, preferably 0.9 to 1.1:1 stoichiometric ratio of meta-phenylenediamine and para-phenylenediamine in NMP. Stoichiometric excess of PDA will result in excess amine linkages. Stoichiometric excess of BPDA is believed preferable to provide excess carboxyl groups which are expected to enhance adhesion of the coating to a polyimide substrate.

The inclusion of one or more diamines or dianhydrides other than those disclosed, e.g. aliphatic diamines or aliphatic dianhydrides or other aromatic diamines and dianhydrides, as reactants in the process may detract from one or more desirable properties of the polymeric products. However, the inclusion of such materials, to the extent that they do not detract substantially from the desirable results obtained with the stated reactants, is contemplated in the formation of the corresponding copolymers.

The reaction to form the polyamic acid is preferably carried out in a polar solvent. The most preferred solvent is n-methyl pyrrolidinone solvent (NMP). However, it is believed that other solvents such as alcohols, ketones, ethers, cyclic amides and dialkylsulfoxides may be employed as well as mixtures of solvents.

EXAMPLE 1

A high-molecular-weight polyamic acid solution according to the invention was synthesized by reacting 3,3',4,4'-biphenyldianhydride (BPDA) with a 1.01:1 stoichiometric ratio of meta-phenylenediamine and para-phenylenediamine in NMP. The acronym "PDA" is used herein to represent the phenylenediamine mixture. This candidate BPDA/PDA polyamic acid coating solution was synthesized as follows. 85.63 g of BPDA was dissolved into 276 g of NMP (from Aldrich) in a 600 ml beaker equipped with a mechanical stirrer at a temperature of about 30° C. 7.80 g of meta-phenylenediamine and 5.19 g para-phenylenediamine were dry mixed, then added to the same 600 ml beaker while stirring. An exothermic reaction immediately began, raising the temperature approximately 20° C. The entire contents of the beaker were then transferred to a 1000 ml round bottom glass reactor equipped with an electrical heating mantle, a mechanical stirrer, a condensor, a drying tube, and a nitrogen purge. The reactor and its contents were then heated while stirring. As the reaction proceeded, the brown, transparent solution became quite viscous as indicated by a substantially diminished vortex. As the reaction proceeded further, an increased vortex appeared indicating a reduction in viscosity. After stirring 1 hour under nitrogen while heating towards reflux, the reactor was permitted to cool. The Brookfield viscosity of the resulting solution was about 575 cP.

EXAMPLE 2

The synthesis of Example 1 was repeated except that samples were withdrawn periodically from the round bottom reactor as the reaction proceeded. The Brookfield viscosity at 50° C. reaction temperature was 39,200 cP. As the reaction temperature rose to 100° C., the solution started to thin out and exhibited a Brookfield viscosity of 5500 cP. As the reaction temperature rose to 140° C., the solution became quite thin as evidenced by the vortex pattern and a Brookfield viscosity of 850 cP. After stirring 1 hour under nitrogen while heating towards reflux, the reactor was permitted to cool. The Brookfield viscosity of the resulting solution was about 800 cP.

EXAMPLE 3

The synthesis of Example 1 was repeated except that only para-phenylenediamine was used.

The protective performance of the coating solution of Example 1 was compared with the following high-temperature polyimide solutions: a PFPI resin formulation (PMDA/4-BDAF, Lot #06-0294-01F) and a another PFPI resin formulation (6FDA/4-BDAF, Lot#12-0994-01F) from TRW, Inc. of Redondo Beach, Calif.

The PFPI resins obtained from TRW are believed to be high-molecular-weight, linear polyimides both containing the 2,2-bis 4-(4-aminophenoxy)-phenyl!hexafluoropropane (4-BDAF) monomer structure. These TRW systems are believed to be based upon 2,2-bis(3',4'-dicarboxyphenyl)hexafluoropropane dianhydride (6FDA) and the 4-BDAF monomer which are very expensive today at more than U.S.$800/kg. In contrast, the BPDA/PDA polyamic acid solution according to the invention provides good thermal stability at reasonable cost. The effectiveness of the coating candidates was evaluated on composite panels that were fabricated from Fiberite (Greenville, Tex.) PMR-15 prepreg reinforced with Celion (Charlotte, N.C.) G30-500 carbon (graphite) fiber. The Celion fiber was sized with EP03 epoxy finish and woven as an eight-harness satin cloth. Standard PMR-15 autoclave cure and oven post-cure cycles were used to fabricate the laminates,

The solids content for all three polyimide solutions was determined by subjecting samples to a 3-h oven exposure at 205° C. (401° F.). The Brookfield viscosity was measured for each solution. A summary of these results can be found in Table 1.

                  TABLE 1                                                          ______________________________________                                         Description of High-Temperature Polyimide Coating                                             AVERAGE   BROOKFIELD                                                           SOLIDS    VISCOSITY                                                            CONTENT   (12 RPM)                                              RESIN TYPE     (WT%)     (cP.)                                                 ______________________________________                                         BPDA/PDA       16          575                                                 6FDA/4-BDAF    25.7      12,000                                                PMDA/4-BDAF    23.4      100,000+                                              (AS-                                                                           RECEIVED)                                                                      PMDA/4-BDAF    12.1       7,500                                                (DILUTED)                                                                      ______________________________________                                    

There is a trade-off between solids content and solution viscosity. For a spray application, it is desirable to keep the solution viscosity under 2,000 cP. For a brush-on coating, a viscosity range between 5,000 and 10,000 cP is preferred. In formulating a coating, the objective is to achieve as high as solids content as possible, but still remain within the viscosity ranges previously described. A high solids content is desirable because more polyimide resin can be placed on the substrate during each coating application. A low viscosity coating solution may facilitate penetration or absorption of the coating into the fiber bundles exposed by machining, thereby providing better sealing of the fiber bundles, and thus better protection of the composite. The low viscosity of the BPDA/PDA coating solution may have facilitated penetration or absorption, e.g. by capillary action, of the coating resin into the fiber bundles exposed by machining, thereby providing better sealing of the fiber bundles.

As shown in Table 1, the Brookfield viscosity of the 16 wt % solids content BPDA/PDA coating solution was measured to be only 575 cP. Ten applications (by brushing) of this BPDA/PDA coating solution were required to obtain the desired coating thickness level on the substrate.

The 6FDA/4-BDAF polyamic acid solution at 25.7 wt % solids was easily applied by brush. Only three applications of this solution were required to reach the desired coating thickness of about 0.075-0.10 mm (or 3-4 mils). The PMDA/4-BDAF solution as received from TRW was so viscous that it would not pour from the container. This polyamic acid solution was diluted down to 12.1 wt % solids with HPLC-grade NMP to obtain a material that could be applied by brush. A total of six applications were needed to form a uniform coating of approximately 4 mils thickness.

Two panels of pre-fabricated carbon fiber/PMR-15 composite laminates were brush-coated with each of the three high-temperature protective coatings. Two additional substrates were left uncoated and used as the controls for the experiment. All of the carbon fiber/PMR-15 panels were solvent wiped, dried at 100° C., grit blasted with 150 silicon carbide grit, water rinsed, then solvent wiped and dried at 100° C., then cooled to room temperature and stored in a dessicator before coating.

After pretreatment, the panels were coated by brushing with the following polyamic acid solutions: BPDA/PDA, PMDA/4-BDAF, or 6FDA/4-BDAF. Each solution was brushed on the substrates by first coating one side of the panel followed by the panel edges. The panels were then placed in an air-recirculating oven for 15 min at each of the following temperatures: 50° C. (122° F.), 75° C. (167° F.), 100° C. (212° F.), 125° C. (257° F.), and finally 150° C. (302° F.). This "pre-bake" allowed the coatings to partially dry by removing most of the NMP solvent and initiated, the imidization reaction of the polyamic acid coating solution.

After the panels were allowed to cool to room temperature, they were turned over and brush-coated on the other side as well as on the edges. This procedure was repeated until the desired weight/thickness was achieved. Approximately a 0.008 mm to 0.025 mm (0.0003 in to 0.001 in or 0.3 mil to 1 mil) thick film was deposited on a composite substrate each time the coating was applied. The edges thus received twice the number of brush-on coatings as did the faces of the samples. A description of the samples and approximate coating thickness can be found in Table 2.

An estimate of the coating thickness was calculated by using a theoretical density of 1.44 g/cc for each polyimide after cure. Additionally, the actual coating thickness was physically measured after the isothermal aging experiment. The "measured" and "estimated" thickness values were found to be in good agreement. Once each substrate reached the desired coating thickness, all of the laminates including the control were cured in an air recirculating oven for 1 h at 100° C. (212° F.) followed by 3 h at 205° C. (401° F.). This was done to completely remove the NMP solvent from the coating layer and to ensure conversion of the polyamic acid to the polyimide. The final coating post-cure cycle consisted of the following time and temperature intervals: 4 h at 121° C. (250° F.), 4 h at 216° C. (420° F.), 8 h at 260° C. (500° F.), 8 h at 288° C. (550° F.), and 8 h at 302° C. (575° F.).

                                      TABLE 2                                      __________________________________________________________________________     Description of High-Temperature Polyimide                                      Brush-Coated Carbon Fiber/PMR-15 Panels.                                                    PANEL                                                                     INITIAL                                                                             THICKNESS          ESTIMATED                                                                             MEASURED                                        PANEL                                                                               WITH   COATING                                                                              COATING                                                                              COATING                                                                               COATING                                         WEIGHT                                                                              COATING                                                                               WEIGHT                                                                               PICK-UP                                                                              THICKNESS                                                                             THICKNESS                               COATING (g)  mm/(mils)                                                                             (g)   (wt. %)                                                                              mm/(mils)                                                                             mm/(mils)                               __________________________________________________________________________     6FDA/4-BDAF                                                                            64.7760                                                                             4.39/(173)                                                                            2.1828                                                                               3.3   0.08/(3.3)                                                                            0.10/(3.8)                              6FDA/4-BDAF                                                                            63.6566                                                                             4.47/(176)                                                                            2.9262                                                                               4.6   0.11/(4.3)                                                                            0.12/(4.6)                              BPDA/PDA                                                                               55.7381                                                                             4.24/(167)                                                                            2.1608                                                                               3.9   0.08/(3.2)                                                                            0.09/(3.6)                              BPDA/PDA                                                                               61.0691                                                                             4.09(161)                                                                             2.5137                                                                               4.1   0.09/(3.4)                                                                            0.10/(4.0)                              PMDA/4-BDAF                                                                            64.1604                                                                             4.52/(178)                                                                            2.2534                                                                               3.5   0.09/(3.4)                                                                            0.10/(3.8)                              PMDA/4-BDAF                                                                            63.0053                                                                             4.45/(175)                                                                            2.4520                                                                               3.9   0.09/(3.7)                                                                            0.11/(4.4)                              CONTROL 53.5461                                                                             3.89/(153                                                                             --    --    --     --                                      __________________________________________________________________________

The coated laminates (and control) were isothermally aged in an open air-recirculating Blue-M oven for 4016 h at 288° C. (550° F.). The exposure temperature was chosen to be approximately 28° C. (50° F.) below the glass-transition temperature of the control panel which was measured at 319° C. (606° F.). Laminates were removed from the oven at different intervals in order to determine weight loss as a function of exposure time.

After isothermal exposure, the laminates were machined into compression (ASTM D695) specimens and tested at room temperature on an Instron Universal Testing Machine.

The physical appearance of each coating after isothermal aging was quite different. The BPDA/PDA and 6FDA/4-BDAF candidates were extremely tough with only minor surface cracks in specific areas of the coating. The PMDA/4-BDAF coating was extremely brittle with severe cracking and peeling.

All of the coating candidates exhibited excellent adhesion integrity of the carbon fiber to resin interface at the substrate edges. The machined surfaces of the composites that were coated demonstrated no sign of flaking or peeling during isothermal exposure. The edge coating could not be pulled or picked off with a razor blade and remained intact after machining the compression test specimens. Visual investigation of the coating surfaces revealed that the 6FDA/4-BDAF candidate and the BPDA/PDA candidate exhibited excellent adhesion to the carbon fiber/PMR-15 composite substrate and all of the coating candidates exhibited excellent adhesion integrity to the machined surfaces of the composite. No flaking or peeling of the edge coating was observed during isothermal aging.

The thermal oxidative stability (TOS) results for the high-temperature coated G30-500/PMR-15 laminates can be found in Table 3. The weight loss data for the coated laminates represents an average value from two panels while the control depicts data from only one panel.

                  TABLE 3                                                          ______________________________________                                         Thermal Oxidative Stability For Coated Celion                                  G30-500/PMR-15 Compression Panels (TOS at 288° C.).                                INITIAL  335 h      620 h 840 h                                     COATING    wt (g)   wt (g)     wt (g)                                                                               wt (g)                                    ______________________________________                                         CONTROL    54.4099  54.2975    54.2071                                                                              54.1345                                   PMDA       66.4138  66.2447    66.1222                                                                              66.0287                                   PMDA       65.4573  65.3073    65.1962                                                                              65.0919                                   6FDA       66.9588  66.7839    66.6683                                                                              66.5802                                   6FDA       66.5828  66.4170    66.3043                                                                              66.2201                                   BPDA       63.2939  63.1740    63.1106                                                                              63.0585                                   BPDA       57.8989  57.8032    57.7452                                                                              57.7014                                   ______________________________________                                    

                  TABLE 3                                                          ______________________________________                                         Continuation of Thermal Oxidative Stability Results For                        Celion G30-500/PMR-15                                                          Compression Panels (TOS at 288° C.)                                                1608 h  2184 h     3258 h                                                                               4016 h                                     COATING    wt (g)  wt (g)     wt (g)                                                                               wt (g)                                     ______________________________________                                         CONTROL    53.8699 53.5988    52.8020                                                                              51.9999                                    PMDA       65.7165 65.3970    64.5400                                                                              --                                         PMDA       64.7505 64.4133    63.3965                                                                              62.4083                                    6FDA       66.2479 65.9442    65.187                                                                               64.402l                                    6FDA       65.9104 65.6117    64.8595                                                                              64.1763                                    BPDA       62.8916 62.7288    62.1875                                                                              61.5769                                    BPDA       57.5591 57.4164    57.008                                                                               56.5596                                    ______________________________________                                    

The TOS results at 288° C. (550° F.) revealed that both the BPDA/PDA coating and the 6FDA/4-BDAF coating offered excellent thermal protection to the G30-500/PMR-15 composite substrate. After 4016 h (167 days or 5.5 months) of isothermal exposure at 288° C. (550° F.), the BPDA/PDA coated substrate lost only 2.5% of its original weight, while the 6FDA/4-BDAF candidate lost 3.7 wt % and the PMDA/4-BDAF candidate lost 4.7 wt %. The PMDA/4-BDAF candidate with 4.7% weight loss showed no benefit in thermal stability over the control panel which had 4.4% weight loss.

Without a protective coating, the carbon fiber/PMR-15 control lost 2.5 wt % in 2934 h. The application of the 6FDA/4-BDAF polyimide coating extended the exposure time (to achieve 2.5% weight loss) to 3159 h, which represents about an 8% improvement in thermal stability. The application of the BPDA/PDA polyimide coating extended the exposure time to reach 2.5% weight loss to 4016 h, which represents nearly a 37% increase in service lifetime of the coated PMR-15 composite at elevated temperature.

After the completion of the isothermal aging, all of the exposed and baseline (not exposed) laminates were subjected to room temperature compression (ASTM D695) testing. The compression data for the coated laminates represents an average value from two panels (4 tests per panel).

As shown in Table 4, the baseline carbon fiber/PMR-15 composite (no exposure and no coating) had a mean compression strength of 91.0 ksi. After 4016 h of thermal exposure at 288° C. (550° F.), compression strength of the control was 62.9 ksi, which represented a 32% decrease. Two of the coated panels (6FDA/4-BDAF and BPDA/PDA) exhibited only a 16% reduction in compression strength after aging, while the PMDA/4-BDAF coating was found to offer no improvement in retained compression strength when compared to the control.

                  TABLE 4                                                          ______________________________________                                         Mean Compression Strength Summmary                                                                       MEAN                                                                           COMPRESSION                                                        ISOTHERMAL  STRENGTH                                             COATING       EXPOSURE    (KSI)                                                ______________________________________                                         NONE          NO          91.0                                                 NONE          YES         62.9                                                 BPDA/PDA      YES         76.9                                                 6FDA/4-BDAF   YES         75.0                                                 PMDA/4-BDAF   YES         61.0                                                 ______________________________________                                    

When designing composite structures for non-load bearing aerospace applications, engineers try to maintain a residual or minimum compression strength of 50 ksi throughout the life of the component. "Useful service lifetime" is therefore defined as the thermo-oxidative exposure time to reach 50 ksi compression strength. A linear relationship appears to exist between mean compression strength and weight loss after 4016 h, 288° C. (550° F.) TOS exposure. A 1% substrate weight loss appears to correspond to approximately a 7 ksi reduction in composite compression strength for the carbon fiber/PMR-15 composites tested. Therefore, a 50 ksi mean compression strength value corresponds to approximately 6.3% in overall composite weight loss. By considering this information and the weight loss prediction results, the service life of non-load bearing carbon fiber/PMR-15 composite structures under 288° C. (550° F.) isothermal exposures can be qualitatively predicted.

For unprotected laminates, the service lifetime at 288° C. (550° F.) would be approximately 4925 h. The 6FDA/4-BDAF coating increased the useful service lifetime to 5700 hours (a 16% gain), whereas the BPDA/PDA coating approached 6875 h which represented a 40% increase. Both coatings offered enhanced thermal protection for carbon fiber/PMR-15 composite substrates by extending the service lifetimes at elevated temperature.

As is known to those skilled in the art, increased adhesion is possible to a substrate that has a chemically active surface. This can best be accomplished by plasma treatment of the substrates after grit-blasting but prior to coating. Plasma variables such as gas type, power level, and reactor residence time would be empirically determined for each system. An increase in adhesion should positively impact the coating performance at elevated temperature.

It is believed that the high temperature service life of any of composites prepared from any of the following high-temperature polyimide matrix resins can be improved by application of a protective coating to the machined edges of fiber reinforced composites. Viable candidates for service at temperatures approaching 371° C. (700° F.) include AFR700B, PMRII-50 and VCAP-75 available from Culver City Composites, Culver City, Calif., MVK-19 available from Maverick Corporation, Cincinnati, Ohio, and SuperImide™ 800 available from The B. F. Goodrich Company, Brecksville, Ohio. 

What is claimed is:
 1. A method of protecting a polyimide matrix article against oxidation comprising:a) synthesizing a coating solution by reacting an aromatic dianhydride with an aromatic diamines, said aromatic diamines including a mixture of para-phenylenediamine and meta-phenylenediamine in a ratio of meta-phenylenediamine to para-phenylenediamine of about 90:10 to about 15:85; and, b) coating said article with said coating solution.
 2. A method as defined in claim 1, wherein said ratio of said meta-phenylenediamine to said para-phenylenediamine is about 75:25 to about 50:50.
 3. A method as defined in claim 1, wherein said aromatic dianhydride being added to said aromatic diamines in a stoichiometric ratio of about 0.8:1 to about 1.2:1.
 4. A method as defined in claim 2, wherein said aromatic dianhydride being added to said aromatic diamines in a stoichiometric ratio of about 0.8:1 to about 1.2:1.
 5. A method as defined in claim 1, wherein said aromatic dianhydride includes biphenyldianhydride.
 6. A method as defined in claim 4, wherein said aromatic dianhydride includes biphenyldianhydride.
 7. A method as defined in claim 1, including the step of adding said aromatic dianhydride and said aromatic diamines to a non-reactive solvent.
 8. A method as defined in claim 6, including the step of adding said aromatic dianhydride and said aromatic diamines to a non-reactive solvent.
 9. A method as defined in claim 7, wherein said solvent includes methyl pyrrolidinone.
 10. A method as defined in claim 1, including the step of heating said aromatic dianhydride and said aromatic diamines to a temperature of about 50° C. to about 150° C., at least until a viscosity drop of said polyamic acid occurs.
 11. A method as defined in claim 8, including the step of heating said aromatic dianhydride and said aromatic diamine to a temperature of about 50° C. to about 150° C., at least until a viscosity drop of said polyamic acid occurs.
 12. A method as defined in claim 10, including the step of heating said aromatic dianhydride and said aromatic diamine for a sufficient time to obtain a polyamic acid having a Brookfield viscosity of about 500 cP to about 5000 cP and a solids content of about 5 to about 35 weight percent.
 13. A method as defined in claim 11, including the step of heating said dianhydride and said aromatic diamines for a sufficient time to obtain a polyamic acid having a Brookfield viscosity of about 500 cP to about 5000 cP and a solids content of about 5 to about 35 weight percent.
 14. A method as defined in claim 12, including the step of heating said dianhydride and said aromatic diamines for a sufficient time to obtain a polyamic acid having a Brookfield viscosity of about 600 cP to about 2000 cP and a solids content of about 10 to about 30 weight percent.
 15. A method as defined in claim 13, including the step of coating said coating solution onto said article to form a coating thickness of about 0.3 mil to about 4 mils.
 16. A method of protecting a polyimide matrix article against oxidation comprising:a) selecting an aromatic dianhydride and an aromatic diamines, said aromatic dianhydride including biphenyldiaxthydride, said aromatic diamines including a mixture of para-phenylenediamine and meta-phenylenediamine, said aromatic dianhydride having a stoichiometric ratio to said aromatic diamine of about 0.8:1 to about 1.2:1, said meta-phenylenediamine and said para-phenylenediamine added in a ratio of about 90:10 to about 15:85; b) mixing together said aromatic dianhydride and said aromatic diamines in a non-reactive solvent to form a reacting solution; c) heating said reacting solution to a temperature of about 50° C. to about 150° C. for a sufficient time to cause the viscosity of said reacting solution to increase and then to decrease until a polyamic acid is formed having a Brookfield viscosity of about 500 cP to about 5000 cP and a solids content of about 5 to about 35 weight percent; and, d) coating said article with said polyamic acid.
 17. A method as defined in claim 16, wherein said ratio of said meta-phenylenediamine to said para-phenylenediamine is about 75:25 to about 50:50.
 18. A method as defined in claim 16, including the step of heating said aromatic dianhydride and said aromatic diamines for a sufficient time to obtain a polyamic acid having a Brookfield viscosity of about 600 cP to about 2000 cP and a solids content of about 10 to about 30 weight percent.
 19. A method as defined in claim 16, wherein the coating thickness is at least about 0.3 mils.
 20. A method as defined in claim 16, including the step of reacting said aromatic dianhydride and said aromatic diamines under a nitrogen atmosphere while heating said aromatic dianhydride and said aromatic diamines to a temperature less than a reflux temperature.
 21. A method as defined in claim 20, including the step of curing said coating to remove said non-reactive solvent, said step of curing including said coated article being heated for at least one hour at a temperature of at least about 100° C., and subsequently heating said coated article at a temperature greater than 100° C. for over one hour.
 22. A method of protecting a polyimide matrix article against oxidation comprising:a) selecting an aromatic dianhydride and an aromatic diamine, b) mixing together said aromatic dianhydride and said aromatic diamine in a non-reacting solvent to form a reacting solution, c) heating said reacting solution for a sufficient time to cause an initial increase in viscosity of said reacting solution and a subsequent decrease in said viscosity of said reacting solution to form a polyamic acid; d) coating said article with at least one coating of said polyamic acid, and e) curing said polyamic acid coating by exposing said coating to an atmosphere for at least one hour at a temperature of at least 100° C.
 23. A method as defined in claim 22, wherein said aromatic dianhydride includes biphenyldianhydride, said aromatic diamine includes a diamine selected from the group consisting of para-phenylenediamine, meta-phenylenediamine and mixtures thereof.
 24. A method as defined in claim 23, wherein said diamine includes meta-phenylenediamine and para-phenylenediamine in a ratio of meta-phenylenediamine to para-phenylenediamine of about 90:10 to about 15:85.
 25. A method as defined in claim 22, wherein said aromatic dianhydride being added to said aromatic diamine in a stoichiometric ratio of about 0.8:1 to about 1.2:1.
 26. A method as defined in claim 24, wherein said aromatic dianhydride being added to said aromatic diamine in a stoichiometric ratio of about 0.8:1 to about 1.2:1.
 27. A method as defined in claim 26, wherein said solvent includes methyl pyrrolidinone.
 28. A method as defined in claim 22, wherein said reacting solution is heated to a temperature of about 50° C. to about 150° C. until said polyamic acid has a Brookfield viscosity of about 500 cP to about 5000 cP and a solids content of about 5 to about 35 weight percent.
 29. A method as defined in claim 23, wherein said reacting solution is heated to a temperature of about 50° C. to about 150° C. until said polyamic acid has a Brookfield viscosity of about 500 cP to about 5000 cP and a solids content of about 5 to about 35 weight percent.
 30. A method as defined in claim 26, wherein said reacting solution is heated to a temperature of about 50° C. to about 150° C. until said polyamic acid has a Brookfield viscosity of about 500 cP to about 5000 cP and a solids content of about 5 to about 35 weight percent.
 31. A method as defined in claim 30, including the step of coating said coating solution onto said article to form a coating thickness of about 0.3 mil to about 4 mils.
 32. A method as defined in claim 28, including the step of reacting said aromatic dianhydride and said aromatic diamine under a nitrogen atmosphere while heating said aromatic dianhydride and said aromatic diamine to a temperature less than a reflux temperature.
 33. A method as defined in claim 30, including the step of reacting said aromatic dianhydride and said aromatic diamine under a nitrogen atmosphere while heating said aromatic dianhydride and said aromatic diamine to a temperature less than a reflux temperature. 